Multibond X-016

PRODUCT DESCRIPTION

Multibond X-016 is a highly water-resistant, two-part cross-linking polyvinyl acetate emulsion adhesive. It is recommended for applications requiring ASTM D5572 wet use performance and DIN EN 204 D4 water-resistance. When mixed with Catalyst A, it develops a water-resistant bond with a light-colored glue line. Multibond X-016 is an excellent choice for finger jointing, cold press, radio-frequency and hot-press applications.

PHYSICAL PROPERTIES

APPLICATION GUIDELINES

Mixing Instructions: The normal recommended portion of catalyst to resin is 5% by volume. A reduced proportion can be used under certain conditions such as burning in a radio frequency press. Mixes containing less than 2.5% by volume should be avoided. Place the resin in mixer and slowly add catalyst while stirring. Continue mixing for five minutes after all the catalyst has been added to ensure a uniform mixture.

Moisture Content: Six to eight percent is the recommended moisture content of the gluing stock. High moisture content will slow down glue line cure and cause weaker than normal adhesive bonds. Additionally, panel shrinkage may occur resulting in stress cracks or end delamination.

Stock Preparation: The preparation of the stock to be glued is extremely important. Joints cut from rip saws should be free of saw marks. They should also be straight and square. Moulded or jointed stock should be free of knife marks. Glazed or burnished joints will prevent glue penetration and should be guarded against. When possible, glue joints should be prepared and glued the same day. The stock should be machined on both top and bottom surfaces to allow even contact with radio frequency platens.

Spread: Generally, 200-245 g/m² of glue line is adequate. Lower adhesive spreads require better stock tolerances and shorter assembly times. Commonly, a mechanical glue spreader is used to apply a uniform spread to the gluing surfaces.

Pressure: Pressure is dependent upon the species or material to be glued and joint preparation. Direct contact of the gluing surfaces must be made to obtain maximum strength. Suggested pressures for various wood densities are: low, 7.0-10.5 Kg/cm²; medium, 8.8-12.3 Kg/cm²; high, 12.3-17.6 Kg/cm². Clamps for edge gluing should be spaced 20-40 cm apart and 5 cm from the end of the panel to evenly distribute pressure along the entire length of the glue line.

RF Cure Time: Radio frequency cure times will vary from machine to machine. Machine manufacturers suggest that machines will cure about 645 cm² of glue line per minute per kilowatt. Glue joints should feel warm immediately after the cure cycle. Cure times should be determined through plant trials.

Finger Jointing: The finger jointing of lumber is increasingly popular as a method of reducing wood waste and providing maximum wood utilization resulting in lower raw material costs. Structural and non-structural finger jointed products have gained wide acceptance throughout the wood industry. The preparation of these joints, as well as the adhesive, plays a critical role in the quality of finger jointed products. Most failures of finger jointed lumber are caused by poorly machined and poorly fitted dry joints. The adhesive plays a role in finger joint back off, heat and water resistance.

Equipment Check: Be sure to check overall knife stack for accuracy. Keep cutterheads in pairs and properly cleaned. Cutterheads should be sharpened as a set. Knife set should cut only .3 mm to .8 mm of wood. Knives should be sharpened after running approximately 70 m3 (wood species may cause this to vary). Make sure cutterhead spindle is set vertically with no wear or play in the bearings. Chain carrier lugs should be squared with the trim saws and cutterheads. Make sure trim saws are set true. Check bed rails for wear on a regular basis. Check hold down pressure to provide sufficient pressure to prevent movement of stock while cutting the joint.

Joint Assembly: Pressure should be held constant until joint is cured. End pressure should be set to provide 10-14Kg/cm² pressure for non-structural joints. Crowder wheels should be aligned to match fingers accurately.

Adhesive Application: Sufficient adhesive spread will provide a uniform coverage that should cover 1/2-2/3 the length of the finger on both sides in a thin continuous film. Make sure fingers aren't skipped and that the adhesive is applied to the whole joint, not just the tips of the fingers. Excess adhesive squeeze-out can cause arcing in a radio frequency tunnel. It also causes adhesive build-up and poor adhesive efficiency. Too much adhesive can cause a hydraulic effect in finger joint back off.

Store in tightly closed original container. Protect from freezing. Storing at temperatures above 25ºC will reduce the maximum storage time. Prolonged storage will result in a gradual increase in viscosity. If thickening, separation or settling occurs, the adhesive should be thoroughly mixed and will then be ready to use again.

IMPORTANT NOTICE TO CUSTOMER:
The recommendations and data contained in this Product Data Sheet for use of this product are based on information Franklin believes to be reliable. They are offered in good faith without guarantee, as conditions and methods for use of our product by Customer and are beyond Franklin’s control. Customer must determine the suitability of the product for a particular application before adopting it on a commercial scale. Discoloration and checking of wood veneer materials may occur with use of the product. These occurrences range in appearance, color and may also vary depending upon the species of wood veneer to which the product is applied. Such discoloration and checking may appear during or after the manufacturing process which utilizes the product. Environmental conditions in some manufacturing plants and end-use locations can contribute to discoloration and checking. Because such discoloration and checking are attributable to conditions beyond Franklin’s control, Franklin cannot assume any responsibility or liability for any discoloration and/or checking problems that might occur.